Incazelo
Usayizi Ojwayelekile
|
Ibanga le-OD(mm) |
Ukubekezela kwe-OD(mm) |
I-ovality |
Khothama |
|
OD Ngaphansi noma kulingana no-5.0 |
±2.00%OD |
2.00% |
0.20% |
|
5.0＜OD＜10.0 |
±1.00%OD |
1.00% |
0.10% |
|
10.0＜OD＜20.0 |
±1.00%OD |
1.00% |
0.10% |
|
20.0＜OD＜30.0 |
±1.00%OD |
1.00% |
0.10% |
|
30.0＜OD＜50.0 |
±1.00%OD |
1.00% |
0.10% |
|
50.0＜OD＜100.0 |
±1.00%OD |
1.00% |
0.15% |
|
100.0＜OD＜160.0 |
±1.00%OD |
1.00% |
0.15% |
Okuqukethwe Ukungcola
|
Ikhodi |
Imibandela |
Al |
Ca |
Cr |
Cu |
Fe |
K |
|
I-PQ191E |
Okujwayelekile |
13.0 |
0.50 |
<0.05 |
<0.05 |
0.10 |
0.10 |
|
Ubuningi |
19.0 |
1.00 |
0.10 |
0.10 |
0.50 |
1.00 |
|
|
I-PQ191EH |
Okujwayelekile |
8.0 |
0.60 |
<0.05 |
<0.01 |
0.10 |
0.10 |
|
Ubuningi |
10.0 |
1.00 |
0.10 |
<0.01 |
0.50 |
0.50 |
|
|
Ikhodi |
Imibandela |
Li |
Mg |
UMn |
Na |
Thi |
Zr |
|
I-PQ191E |
Okujwayelekile |
0.3 |
0.05 |
0.05 |
0.10 |
1.30 |
1.00 |
|
Ubuningi |
1.00 |
0.20 |
0.20 |
1.00 |
2.00 |
2.00 |
|
|
I-PQ191EH |
Okujwayelekile |
0.20 |
0.05 |
0.05 |
0.10 |
1.30 |
1.00 |
|
Ubuningi |
0.50 |
0.20 |
0.20 |
0.50 |
2.00 |
2.00 |
Izakhiwo
- Ukwenza ngokwezifiso Ukuguquguquka
- - Ukuqinisekiswa Kwekhwalithi Ephezulu
- Izindleko - Ukusebenza Okuphumelelayo
- Ukulethwa Okusheshayo Nokuthembekile
Izindawo Zokufaka Isicelo
- Imboni ye-Petrochemical
- Imboni Yezokwelapha
- Ubunjiniyela Bemvelo
Izakhiwo
|
Izakhiwo Zomzimba |
Amanani |
|
Ubumsulwa |
＞99.99% |
|
Ukuminyana |
2.2g/cm3 |
|
Ukungafihli |
＞90% |
|
Mohs Ukuqina |
5.5--6.5 |
|
I-Deformation Point |
1280 degree |
|
Iphuzu lokuthambisa |
1750 degree |
|
I-Annealing Point |
1250 degree |
|
Ukushisa Okuthile (20 - 350℃) |
670J/kg. iziqu |
|
I-Thermal Conductivity (20 degree) |
1.4W/m. iziqu |
|
I-Heat Conductivity (w/mk,1000 degree) |
1.0-1.2 |
|
I-Refractive Index |
1.4585 |
|
I-Coefficient of Thermal Expansion |
5.510 -7cm/cm. iziqu |
|
Okushisayo - kweTemperature yokusebenza |
1750--2050 degree |
|
Ithemu Elifushane - Lethempelesha Yesevisi |
1450 degree |
|
Ithempelesha Yesevisi yesikhathi eside engu-- |
1100 degree |
|
Chemical Properties |
Amanani |
|
Ukumelana ne-Acid |
I-Acid Eqinile(ngaphandle kwe-HF),i-alkali eqinile, isixazululo sezinto eziphilayo |
|
Amazinga okushisa aphezulu Imelana nokugqwala |
Kuhle kakhulu |
|
Okuqukethwe Kwensimbi Engcolile |
5 ppm |
|
Izakhiwo zikagesi |
Amanani |
|
Ukungazweli |
7107Ω.cm |
|
Amandla e-Insulation |
250~400Kv/cm |
|
I-Dielectric Constant |
3.7~3.9 |
|
I-Dielectric Absorption Coefficient |
＜410-4 |
|
I-Dielectric Loss Coefficient |
＜110-4 |
|
Izakhiwo Zemishini |
Amanani |
|
Amandla Acindezelayo |
1100MPa |
|
Ukugoba Amandla |
67MPa |
|
Amandla Okuqina |
48MPa |
|
Isilinganiso sikaPoisson |
0.14~0.17 |
|
I-Modulus Encane |
72000MPa |
|
Shear Modulus |
31000MPa |
FAQ
Q: Yimaphi ama-diameter kanye nokubekezelelana okukhona?
A: Ibanga elijwayelekile:
- Ububanzi: 1mm–150mm (±0.05mm)
- Ubude: kufika ku-2000mm (±1mm)
- Osayizi bangokwezifiso abanokubekezelelana okuqinile (±0.01mm)
Q: Ingabe izinduku ze-quartz zingenziwa ngomshini ngemva kokulethwa?
A: Yebo, sincoma:
- Ithuluzi ledayimane lokusika
- CO₂ laser drilling (for holes >0.5mm)
- Ukupholishwa komlilo kokwelapha emaphethelweni
Q: Ingabe izinduku zakho ze-quartz zilungele iziqondiso zokukhanya kwe-UV?
A: Yebo, nge:
- >90% ukudluliswa @185nm (UV grade)
- Izindawo ozikhethela zona ezicwebezeliswe kakhulu (Ra<1nm)
Q: Zipakishwa kanjani izinduku ukuvimbela umonakalo?
A: Ukuvikelwa{0}}kwezendlalelo eziningi:
- Imikhono ye-PVC ngayinye
- Amakhreyithi okhuni ahlukaniswe igwebu{1}
- Izikhwama zokuvikela umswakama-(i-nitrogen purge)
Amashadi ashisayo: i-quartz rod, China abakhiqizi benduku ye-quartz, abahlinzeki, imboni
Thumela ukuPhenya
Ungahle Uthande